MakeItFrom.com
Menu (ESC)

ASTM A182 Grade F10 vs. EN 1.8961 Steel

Both ASTM A182 grade F10 and EN 1.8961 steel are iron alloys. They have 71% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F10 and the bottom bar is EN 1.8961 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
130
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 34
19
Fatigue Strength, MPa 180
150
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
270
Tensile Strength: Ultimate (UTS), MPa 630
430
Tensile Strength: Yield (Proof), MPa 230
220

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 600
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 17
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 18
2.6
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.6
1.7
Embodied Energy, MJ/kg 51
23
Embodied Water, L/kg 120
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
70
Resilience: Unit (Modulus of Resilience), kJ/m3 140
130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
15
Strength to Weight: Bending, points 21
16
Thermal Shock Resistance, points 18
13

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Carbon (C), % 0.1 to 0.2
0 to 0.16
Chromium (Cr), % 7.0 to 9.0
0.35 to 0.85
Copper (Cu), % 0
0.2 to 0.6
Iron (Fe), % 66.5 to 72.4
96.1 to 99.3
Manganese (Mn), % 0.5 to 0.8
0.15 to 0.7
Nickel (Ni), % 19 to 22
0 to 0.7
Niobium (Nb), % 0
0 to 0.065
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 1.0 to 1.4
0 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.035
Titanium (Ti), % 0
0 to 0.12
Vanadium (V), % 0
0 to 0.14