ASTM A182 Grade F10 vs. Grade TDC Steel
Both ASTM A182 grade F10 and grade TDC steel are iron alloys. They have 71% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F10 and the bottom bar is grade TDC steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 510 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 56 | |
| 50 |
| Shear Modulus, GPa | 74 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 1700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1450 |
| Melting Onset (Solidus), °C | 1370 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 1.9 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 51 | |
| 19 |
| Embodied Water, L/kg | 120 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 60 |
| Strength to Weight: Bending, points | 21 | |
| 40 |
| Thermal Shock Resistance, points | 18 | |
| 50 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0.6 to 0.75 |
| Chromium (Cr), % | 7.0 to 9.0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 66.5 to 72.4 | |
| 98 to 99.4 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.5 to 1.2 |
| Nickel (Ni), % | 19 to 22 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 1.0 to 1.4 | |
| 0.1 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |