ASTM A182 Grade F10 vs. C69400 Brass
ASTM A182 grade F10 belongs to the iron alloys classification, while C69400 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F10 and the bottom bar is C69400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 34 | |
| 17 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 74 | |
| 42 |
| Shear Strength, MPa | 420 | |
| 350 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 170 |
| Melting Completion (Liquidus), °C | 1420 | |
| 920 |
| Melting Onset (Solidus), °C | 1370 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 410 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 6.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 6.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 27 |
| Density, g/cm3 | 7.9 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 51 | |
| 44 |
| Embodied Water, L/kg | 120 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 340 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 22 | |
| 19 |
| Strength to Weight: Bending, points | 21 | |
| 18 |
| Thermal Shock Resistance, points | 18 | |
| 20 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0 |
| Chromium (Cr), % | 7.0 to 9.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 80 to 83 |
| Iron (Fe), % | 66.5 to 72.4 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 |
| Nickel (Ni), % | 19 to 22 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 1.0 to 1.4 | |
| 3.5 to 4.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 11.5 to 16.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |