ASTM A182 Grade F10 vs. C91600 Bronze

ASTM A182 grade F10 belongs to the iron alloys classification, while C91600 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F10 and the bottom bar is C91600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
84
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 34
11
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
41
Tensile Strength: Ultimate (UTS), MPa 630
310
Tensile Strength: Yield (Proof), MPa 230
160

Thermal Properties

Latent Heat of Fusion, J/g 290
190
Maximum Temperature: Mechanical, °C 600
170
Melting Completion (Liquidus), °C 1420
1030
Melting Onset (Solidus), °C 1370
860
Specific Heat Capacity, J/kg-K 470
370
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
10
Electrical Conductivity: Equal Weight (Specific), % IACS 17
10

Otherwise Unclassified Properties

Base Metal Price, % relative 18
36
Density, g/cm3 7.9
8.8
Embodied Carbon, kg CO2/kg material 3.6
3.7
Embodied Energy, MJ/kg 51
61
Embodied Water, L/kg 120
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
30
Resilience: Unit (Modulus of Resilience), kJ/m3 140
120
Stiffness to Weight: Axial, points 13
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 22
9.9
Strength to Weight: Bending, points 21
12
Thermal Shock Resistance, points 18
11

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Carbon (C), % 0.1 to 0.2
0
Chromium (Cr), % 7.0 to 9.0
0
Copper (Cu), % 0
85.9 to 89.1
Iron (Fe), % 66.5 to 72.4
0 to 0.2
Lead (Pb), % 0
0 to 0.25
Manganese (Mn), % 0.5 to 0.8
0
Nickel (Ni), % 19 to 22
1.2 to 2.0
Phosphorus (P), % 0 to 0.040
0 to 0.3
Silicon (Si), % 1.0 to 1.4
0 to 0.0050
Sulfur (S), % 0 to 0.030
0 to 0.050
Tin (Sn), % 0
9.7 to 10.8
Zinc (Zn), % 0
0 to 0.25