ASTM A182 Grade F11 Class 1 vs. EN 1.4460 Stainless Steel

Both ASTM A182 grade F11 class 1 and EN 1.4460 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F11 class 1 and the bottom bar is EN 1.4460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
21
Fatigue Strength, MPa 160
330
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 300
470
Tensile Strength: Ultimate (UTS), MPa 470
750
Tensile Strength: Yield (Proof), MPa 230
510

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
18
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
3.4
Embodied Energy, MJ/kg 21
48
Embodied Water, L/kg 52
180

Common Calculations

PREN (Pitting Resistance) 3.0
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 89
140
Resilience: Unit (Modulus of Resilience), kJ/m3 140
640
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
27
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 14
20

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.050
Chromium (Cr), % 1.0 to 1.5
25 to 28
Iron (Fe), % 96 to 97.7
60.2 to 69.2
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.44 to 0.65
1.3 to 2.0
Nickel (Ni), % 0
4.5 to 6.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.5 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015