ASTM A182 Grade F11 Class 2 vs. ASTM Grade HP Steel
Both ASTM A182 grade F11 class 2 and ASTM grade HP steel are iron alloys. They have a modest 39% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F11 class 2 and the bottom bar is ASTM grade HP steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 22 | |
| 5.1 |
| Fatigue Strength, MPa | 220 | |
| 130 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1370 |
| Melting Onset (Solidus), °C | 1420 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 39 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.9 | |
| 34 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 5.8 |
| Embodied Energy, MJ/kg | 21 | |
| 82 |
| Embodied Water, L/kg | 53 | |
| 220 |
Common Calculations
| PREN (Pitting Resistance) | 3.0 | |
| 27 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 21 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 170 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 19 | |
| 17 |
| Strength to Weight: Bending, points | 19 | |
| 17 |
| Thermal Diffusivity, mm2/s | 11 | |
| 3.2 |
| Thermal Shock Resistance, points | 16 | |
| 11 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0.35 to 0.75 |
| Chromium (Cr), % | 1.0 to 1.5 | |
| 24 to 28 |
| Iron (Fe), % | 95.8 to 97.7 | |
| 29.2 to 42.7 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.44 to 0.65 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 33 to 37 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.5 to 1.0 | |
| 0 to 2.5 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.040 |