ASTM A182 Grade F12 Class 1 vs. EN 1.4116 Stainless Steel

Both ASTM A182 grade F12 class 1 and EN 1.4116 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 86% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 1 and the bottom bar is EN 1.4116 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
240
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
14
Fatigue Strength, MPa 180
240
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 300
450
Tensile Strength: Ultimate (UTS), MPa 470
750
Tensile Strength: Yield (Proof), MPa 250
430

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 430
800
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 45
30
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
8.0
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.5
Embodied Energy, MJ/kg 21
36
Embodied Water, L/kg 52
110

Common Calculations

PREN (Pitting Resistance) 2.8
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
87
Resilience: Unit (Modulus of Resilience), kJ/m3 160
470
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
27
Strength to Weight: Bending, points 17
24
Thermal Diffusivity, mm2/s 12
8.1
Thermal Shock Resistance, points 14
26

Alloy Composition

Carbon (C), % 0.050 to 0.15
0.45 to 0.55
Chromium (Cr), % 0.8 to 1.3
14 to 15
Iron (Fe), % 96.8 to 98.4
81.3 to 85
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.44 to 0.65
0.5 to 0.8
Nitrogen (N), % 0
0 to 0.15
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.015
Vanadium (V), % 0
0.1 to 0.2