ASTM A182 Grade F12 Class 1 vs. EN 2.4642 Nickel

ASTM A182 grade F12 class 1 belongs to the iron alloys classification, while EN 2.4642 nickel belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 1 and the bottom bar is EN 2.4642 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
34
Fatigue Strength, MPa 180
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 300
450
Tensile Strength: Ultimate (UTS), MPa 470
670
Tensile Strength: Yield (Proof), MPa 250
270

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 430
1010
Melting Completion (Liquidus), °C 1470
1360
Melting Onset (Solidus), °C 1420
1320
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
12
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
50
Density, g/cm3 7.9
8.3
Embodied Carbon, kg CO2/kg material 1.6
8.2
Embodied Energy, MJ/kg 21
120
Embodied Water, L/kg 52
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91
180
Resilience: Unit (Modulus of Resilience), kJ/m3 160
180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 17
21
Thermal Diffusivity, mm2/s 12
3.1
Thermal Shock Resistance, points 14
18

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Carbon (C), % 0.050 to 0.15
0 to 0.050
Chromium (Cr), % 0.8 to 1.3
27 to 31
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 96.8 to 98.4
7.0 to 11
Manganese (Mn), % 0.3 to 0.6
0 to 0.5
Molybdenum (Mo), % 0.44 to 0.65
0
Nickel (Ni), % 0
55.9 to 66
Phosphorus (P), % 0 to 0.045
0 to 0.020
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.045
0 to 0.015