ASTM A182 Grade F12 Class 2 vs. SAE-AISI 1064 Steel
Both ASTM A182 grade F12 class 2 and SAE-AISI 1064 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is SAE-AISI 1064 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 22 | |
| 12 to 13 |
| Fatigue Strength, MPa | 220 | |
| 300 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 34 | |
| 42 to 43 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 340 | |
| 430 to 440 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 720 to 730 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 470 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 43 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 21 | |
| 19 |
| Embodied Water, L/kg | 52 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 79 to 81 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 600 to 630 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 25 to 26 |
| Strength to Weight: Bending, points | 19 | |
| 23 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 16 | |
| 25 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0.6 to 0.7 |
| Chromium (Cr), % | 0.8 to 1.3 | |
| 0 |
| Iron (Fe), % | 96.4 to 98.3 | |
| 98.4 to 98.9 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0.44 to 0.65 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.1 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.050 |