ASTM A182 Grade F12 Class 2 vs. SAE-AISI 12L14 Steel
Both ASTM A182 grade F12 class 2 and SAE-AISI 12L14 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is SAE-AISI 12L14 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 140 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 22 | |
| 11 to 25 |
| Fatigue Strength, MPa | 220 | |
| 190 to 290 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 34 | |
| 39 to 51 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 340 | |
| 280 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 440 to 620 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 260 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 43 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 21 | |
| 18 |
| Embodied Water, L/kg | 52 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 64 to 93 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 | |
| 180 to 560 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 15 to 22 |
| Strength to Weight: Bending, points | 19 | |
| 16 to 20 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 16 | |
| 14 to 20 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0.8 to 1.3 | |
| 0 |
| Iron (Fe), % | 96.4 to 98.3 | |
| 97.9 to 98.7 |
| Lead (Pb), % | 0 | |
| 0.15 to 0.35 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0.85 to 1.2 |
| Molybdenum (Mo), % | 0.44 to 0.65 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0.040 to 0.090 |
| Silicon (Si), % | 0.1 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0.26 to 0.35 |