ASTM A182 Grade F122 vs. EN 1.4432 Stainless Steel

Both ASTM A182 grade F122 and EN 1.4432 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F122 and the bottom bar is EN 1.4432 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
44
Fatigue Strength, MPa 320
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
78
Shear Strength, MPa 450
420
Tensile Strength: Ultimate (UTS), MPa 710
610
Tensile Strength: Yield (Proof), MPa 450
250

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Mechanical, °C 600
960
Melting Completion (Liquidus), °C 1490
1450
Melting Onset (Solidus), °C 1440
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 24
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 12
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 12
19
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 3.0
3.9
Embodied Energy, MJ/kg 44
54
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 17
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
220
Resilience: Unit (Modulus of Resilience), kJ/m3 520
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 6.4
4.0
Thermal Shock Resistance, points 19
14

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0.070 to 0.14
0 to 0.030
Chromium (Cr), % 10 to 11.5
16.5 to 18.5
Copper (Cu), % 0.3 to 1.7
0
Iron (Fe), % 81.3 to 87.7
62.3 to 70.5
Manganese (Mn), % 0 to 0.7
0 to 2.0
Molybdenum (Mo), % 0.25 to 0.6
2.5 to 3.0
Nickel (Ni), % 0 to 0.5
10.5 to 13
Niobium (Nb), % 0.040 to 0.1
0
Nitrogen (N), % 0.040 to 0.1
0 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 1.5 to 2.5
0
Vanadium (V), % 0.15 to 0.3
0
Zirconium (Zr), % 0 to 0.010
0