ASTM A182 Grade F22V vs. EN 1.4347 Stainless Steel

Both ASTM A182 grade F22V and EN 1.4347 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F22V and the bottom bar is EN 1.4347 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
23
Fatigue Strength, MPa 320
320
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
79
Tensile Strength: Ultimate (UTS), MPa 670
660
Tensile Strength: Yield (Proof), MPa 460
480

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 460
1100
Melting Completion (Liquidus), °C 1470
1410
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 4.2
16
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 2.5
3.1
Embodied Energy, MJ/kg 35
44
Embodied Water, L/kg 61
170

Common Calculations

PREN (Pitting Resistance) 5.6
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
140
Resilience: Unit (Modulus of Resilience), kJ/m3 570
570
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
24
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 19
19

Alloy Composition

Boron (B), % 0 to 0.0020
0
Calcium (Ca), % 0 to 0.015
0
Carbon (C), % 0.11 to 0.15
0 to 0.050
Chromium (Cr), % 2.0 to 2.5
25 to 27
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 94.6 to 96.4
62.2 to 69.4
Manganese (Mn), % 0.3 to 0.6
0 to 1.5
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0 to 0.25
5.5 to 7.5
Niobium (Nb), % 0 to 0.070
0
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.015
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 1.5
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0.25 to 0.35
0