ASTM A182 Grade F22V vs. C91600 Bronze

ASTM A182 grade F22V belongs to the iron alloys classification, while C91600 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F22V and the bottom bar is C91600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
84
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 21
11
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
41
Tensile Strength: Ultimate (UTS), MPa 670
310
Tensile Strength: Yield (Proof), MPa 460
160

Thermal Properties

Latent Heat of Fusion, J/g 250
190
Maximum Temperature: Mechanical, °C 460
170
Melting Completion (Liquidus), °C 1470
1030
Melting Onset (Solidus), °C 1430
860
Specific Heat Capacity, J/kg-K 470
370
Thermal Conductivity, W/m-K 39
71
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
10

Otherwise Unclassified Properties

Base Metal Price, % relative 4.2
36
Density, g/cm3 7.9
8.8
Embodied Carbon, kg CO2/kg material 2.5
3.7
Embodied Energy, MJ/kg 35
61
Embodied Water, L/kg 61
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
30
Resilience: Unit (Modulus of Resilience), kJ/m3 570
120
Stiffness to Weight: Axial, points 13
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 24
9.9
Strength to Weight: Bending, points 22
12
Thermal Diffusivity, mm2/s 11
22
Thermal Shock Resistance, points 19
11

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Boron (B), % 0 to 0.0020
0
Calcium (Ca), % 0 to 0.015
0
Carbon (C), % 0.11 to 0.15
0
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.2
85.9 to 89.1
Iron (Fe), % 94.6 to 96.4
0 to 0.2
Lead (Pb), % 0
0 to 0.25
Manganese (Mn), % 0.3 to 0.6
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0 to 0.25
1.2 to 2.0
Niobium (Nb), % 0 to 0.070
0
Phosphorus (P), % 0 to 0.015
0 to 0.3
Silicon (Si), % 0 to 0.1
0 to 0.0050
Sulfur (S), % 0 to 0.010
0 to 0.050
Tin (Sn), % 0
9.7 to 10.8
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0.25 to 0.35
0
Zinc (Zn), % 0
0 to 0.25