ASTM A182 Grade F24 vs. EN 1.6571 Steel

Both ASTM A182 grade F24 and EN 1.6571 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.6571 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
160 to 190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 670
520 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
420
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
3.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.7
Embodied Energy, MJ/kg 33
22
Embodied Water, L/kg 61
53

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
19 to 51
Strength to Weight: Bending, points 22
18 to 36
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 19
15 to 43

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.16 to 0.23
Chromium (Cr), % 2.2 to 2.6
0.6 to 0.9
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 94.5 to 96.1
95.3 to 97.1
Manganese (Mn), % 0.3 to 0.7
0.5 to 0.9
Molybdenum (Mo), % 0.9 to 1.1
0.25 to 0.35
Nickel (Ni), % 0
1.4 to 1.7
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.45
0 to 0.3
Sulfur (S), % 0 to 0.010
0.020 to 0.040
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0