ASTM A182 Grade F3V vs. EN 1.7033 Steel

Both ASTM A182 grade F3V and EN 1.7033 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3V and the bottom bar is EN 1.7033 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
150 to 240
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 660
500 to 1720

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 470
420
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
45
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.2
2.2
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
19
Embodied Water, L/kg 63
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
18 to 61
Strength to Weight: Bending, points 21
18 to 41
Thermal Diffusivity, mm2/s 10
12
Thermal Shock Resistance, points 19
15 to 50

Alloy Composition

Boron (B), % 0.0010 to 0.0030
0
Carbon (C), % 0.050 to 0.18
0.3 to 0.37
Chromium (Cr), % 2.8 to 3.2
0.9 to 1.2
Iron (Fe), % 94.4 to 95.7
97.1 to 98.2
Manganese (Mn), % 0.3 to 0.6
0.6 to 0.9
Molybdenum (Mo), % 0.9 to 1.1
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.1
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.035
Titanium (Ti), % 0.015 to 0.035
0
Vanadium (V), % 0.2 to 0.3
0