ASTM A182 Grade F3V vs. SAE-AISI 4817 Steel

Both ASTM A182 grade F3V and SAE-AISI 4817 steel are iron alloys. Both are furnished in the annealed condition. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3V and the bottom bar is SAE-AISI 4817 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
23
Fatigue Strength, MPa 330
270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 410
350
Tensile Strength: Ultimate (UTS), MPa 660
560
Tensile Strength: Yield (Proof), MPa 470
370

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 470
410
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 4.2
4.3
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.8
Embodied Energy, MJ/kg 33
24
Embodied Water, L/kg 63
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 590
370
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23
20
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 10
14
Thermal Shock Resistance, points 19
17

Alloy Composition

Boron (B), % 0.0010 to 0.0030
0
Carbon (C), % 0.050 to 0.18
0.15 to 0.2
Chromium (Cr), % 2.8 to 3.2
0
Iron (Fe), % 94.4 to 95.7
94.7 to 95.9
Manganese (Mn), % 0.3 to 0.6
0.4 to 0.6
Molybdenum (Mo), % 0.9 to 1.1
0.2 to 0.3
Nickel (Ni), % 0
3.3 to 3.8
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.1
0.15 to 0.35
Sulfur (S), % 0 to 0.020
0 to 0.040
Titanium (Ti), % 0.015 to 0.035
0
Vanadium (V), % 0.2 to 0.3
0