ASTM A182 Grade F5 vs. EN 1.0225 Steel

Both ASTM A182 grade F5 and EN 1.0225 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F5 and the bottom bar is EN 1.0225 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130 to 140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
6.7 to 24
Fatigue Strength, MPa 220
170 to 220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 340
280 to 290
Tensile Strength: Ultimate (UTS), MPa 540
440 to 500
Tensile Strength: Yield (Proof), MPa 310
230 to 380

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 9.4
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 24
18
Embodied Water, L/kg 69
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
31 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 260
140 to 390
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
16 to 18
Strength to Weight: Bending, points 19
16 to 18
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 15
14 to 16

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.21
Chromium (Cr), % 4.0 to 6.0
0
Iron (Fe), % 91.5 to 95.3
98 to 100
Manganese (Mn), % 0.3 to 0.6
0 to 1.4
Molybdenum (Mo), % 0.44 to 0.65
0
Nickel (Ni), % 0 to 0.5
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.045