ASTM A182 Grade F6b vs. EN 1.3537 Steel
Both ASTM A182 grade F6b and EN 1.3537 steel are iron alloys. They have 87% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F6b and the bottom bar is EN 1.3537 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 260 | |
| 190 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 620 to 730 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 440 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1450 |
| Melting Onset (Solidus), °C | 1400 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 25 | |
| 43 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.8 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 8.0 | |
| 2.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 1.5 |
| Embodied Energy, MJ/kg | 30 | |
| 21 |
| Embodied Water, L/kg | 100 | |
| 54 |
Common Calculations
| PREN (Pitting Resistance) | 14 | |
| 2.6 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 30 | |
| 22 to 26 |
| Strength to Weight: Bending, points | 26 | |
| 21 to 23 |
| Thermal Diffusivity, mm2/s | 6.7 | |
| 12 |
| Thermal Shock Resistance, points | 31 | |
| 18 to 22 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 to 0.15 | |
| 0.93 to 1.1 |
| Chromium (Cr), % | 11.5 to 13.5 | |
| 1.7 to 2.0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.3 |
| Iron (Fe), % | 81.2 to 87.1 | |
| 96.4 to 97.8 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.25 to 0.45 |
| Molybdenum (Mo), % | 0.4 to 0.6 | |
| 0.15 to 0.3 |
| Nickel (Ni), % | 1.0 to 2.0 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.0015 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.15 to 0.45 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |