ASTM A182 Grade F911 vs. EN 1.0258 Steel

Both ASTM A182 grade F911 and EN 1.0258 steel are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F911 and the bottom bar is EN 1.0258 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
23
Fatigue Strength, MPa 350
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 430
310
Tensile Strength: Ultimate (UTS), MPa 690
490
Tensile Strength: Yield (Proof), MPa 500
290

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 600
400
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1440
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
49
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.1
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 40
19
Embodied Water, L/kg 90
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
95
Resilience: Unit (Modulus of Resilience), kJ/m3 650
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 6.9
13
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.00030 to 0.0060
0
Carbon (C), % 0.090 to 0.13
0 to 0.2
Chromium (Cr), % 8.5 to 9.5
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 86.2 to 88.9
96.9 to 100
Manganese (Mn), % 0.3 to 0.6
0 to 1.4
Molybdenum (Mo), % 0.9 to 1.1
0 to 0.080
Nickel (Ni), % 0 to 0.4
0 to 0.3
Niobium (Nb), % 0.060 to 0.1
0 to 0.010
Nitrogen (N), % 0.040 to 0.090
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.1 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0 to 0.010
0 to 0.040
Tungsten (W), % 0.9 to 1.1
0
Vanadium (V), % 0.18 to 0.25
0 to 0.020
Zirconium (Zr), % 0 to 0.010
0