ASTM A182 Grade F911 vs. SAE-AISI 8625 Steel

Both ASTM A182 grade F911 and SAE-AISI 8625 steel are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F911 and the bottom bar is SAE-AISI 8625 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
25
Fatigue Strength, MPa 350
240
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 430
330
Tensile Strength: Ultimate (UTS), MPa 690
510
Tensile Strength: Yield (Proof), MPa 500
330

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 600
410
Melting Completion (Liquidus), °C 1480
1460
Melting Onset (Solidus), °C 1440
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
39
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.6
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 40
20
Embodied Water, L/kg 90
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
110
Resilience: Unit (Modulus of Resilience), kJ/m3 650
300
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 6.9
10
Thermal Shock Resistance, points 19
17

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.00030 to 0.0060
0
Carbon (C), % 0.090 to 0.13
0.23 to 0.28
Chromium (Cr), % 8.5 to 9.5
0.4 to 0.6
Iron (Fe), % 86.2 to 88.9
96.8 to 98
Manganese (Mn), % 0.3 to 0.6
0.7 to 0.9
Molybdenum (Mo), % 0.9 to 1.1
0.15 to 0.25
Nickel (Ni), % 0 to 0.4
0.4 to 0.7
Niobium (Nb), % 0.060 to 0.1
0
Nitrogen (N), % 0.040 to 0.090
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0.1 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.040
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0.9 to 1.1
0
Vanadium (V), % 0.18 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0