ASTM A182 Grade F92 vs. EN 1.4835 Stainless Steel

Both ASTM A182 grade F92 and EN 1.4835 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F92 and the bottom bar is EN 1.4835 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
43
Fatigue Strength, MPa 360
310
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 440
520
Tensile Strength: Ultimate (UTS), MPa 690
750
Tensile Strength: Yield (Proof), MPa 500
350

Thermal Properties

Latent Heat of Fusion, J/g 260
320
Maximum Temperature: Mechanical, °C 590
1150
Melting Completion (Liquidus), °C 1490
1400
Melting Onset (Solidus), °C 1450
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 26
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 10
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 11
17
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 2.8
3.3
Embodied Energy, MJ/kg 40
47
Embodied Water, L/kg 89
160

Common Calculations

PREN (Pitting Resistance) 14
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
270
Resilience: Unit (Modulus of Resilience), kJ/m3 650
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
27
Strength to Weight: Bending, points 22
24
Thermal Diffusivity, mm2/s 6.9
4.0
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.070 to 0.13
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 8.5 to 9.5
20 to 22
Iron (Fe), % 85.8 to 89.1
62 to 68.4
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0.3 to 0.6
0
Nickel (Ni), % 0 to 0.4
10 to 12
Niobium (Nb), % 0.040 to 0.090
0
Nitrogen (N), % 0.030 to 0.070
0.12 to 0.2
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0 to 0.5
1.4 to 2.5
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 1.5 to 2.0
0
Vanadium (V), % 0.15 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0