ASTM A182 Grade F92 vs. Grade 7 Babbitt Metal
ASTM A182 grade F92 belongs to the iron alloys classification, while grade 7 Babbitt Metal belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F92 and the bottom bar is grade 7 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 240 | |
23 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
26 |
Poisson's Ratio | 0.28 | |
0.4 |
Shear Modulus, GPa | 76 | |
9.1 |
Tensile Strength: Yield (Proof), MPa | 500 | |
25 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
48 |
Melting Completion (Liquidus), °C | 1490 | |
270 |
Melting Onset (Solidus), °C | 1450 | |
240 |
Specific Heat Capacity, J/kg-K | 470 | |
150 |
Thermal Expansion, µm/m-K | 13 | |
26 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 11 | |
23 |
Density, g/cm3 | 7.9 | |
10 |
Embodied Carbon, kg CO2/kg material | 2.8 | |
4.4 |
Embodied Energy, MJ/kg | 40 | |
62 |
Embodied Water, L/kg | 89 | |
880 |
Common Calculations
Resilience: Unit (Modulus of Resilience), kJ/m3 | 650 | |
12 |
Stiffness to Weight: Axial, points | 14 | |
1.4 |
Stiffness to Weight: Bending, points | 24 | |
9.6 |
Alloy Composition
Aluminum (Al), % | 0 to 0.020 | |
0 to 0.0050 |
Antimony (Sb), % | 0 | |
14 to 16 |
Arsenic (As), % | 0 | |
0.3 to 0.6 |
Bismuth (Bi), % | 0 | |
0 to 0.1 |
Boron (B), % | 0.0010 to 0.0060 | |
0 |
Cadmium (Cd), % | 0 | |
0 to 0.050 |
Carbon (C), % | 0.070 to 0.13 | |
0 |
Chromium (Cr), % | 8.5 to 9.5 | |
0 |
Copper (Cu), % | 0 | |
0 to 0.5 |
Iron (Fe), % | 85.8 to 89.1 | |
0 to 0.1 |
Lead (Pb), % | 0 | |
71.9 to 76.4 |
Manganese (Mn), % | 0.3 to 0.6 | |
0 |
Molybdenum (Mo), % | 0.3 to 0.6 | |
0 |
Nickel (Ni), % | 0 to 0.4 | |
0 |
Niobium (Nb), % | 0.040 to 0.090 | |
0 |
Nitrogen (N), % | 0.030 to 0.070 | |
0 |
Phosphorus (P), % | 0 to 0.020 | |
0 |
Silicon (Si), % | 0 to 0.5 | |
0 |
Sulfur (S), % | 0 to 0.010 | |
0 |
Tin (Sn), % | 0 | |
9.3 to 10.7 |
Titanium (Ti), % | 0 to 0.010 | |
0 |
Tungsten (W), % | 1.5 to 2.0 | |
0 |
Vanadium (V), % | 0.15 to 0.25 | |
0 |
Zinc (Zn), % | 0 | |
0 to 0.0050 |
Zirconium (Zr), % | 0 to 0.010 | |
0 |