ASTM A204 Steel vs. 92-silver 8-tin-oxide
ASTM A204 steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is ASTM A204 steel and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 76 to 80 |
| Elongation at Break, % | 18 to 22 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 95 | |
| 62 to 110 |
| Shear Strength, MPa | 330 to 360 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 590 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 290 to 330 | |
| 120 to 300 |