ASTM A204 Steel vs. N07041 Nickel

ASTM A204 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ASTM A204 steel and the bottom bar is N07041 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 18 to 22
14
Fatigue Strength, MPa 200 to 220
540
Shear Strength, MPa 330 to 360
850
Tensile Strength: Ultimate (UTS), MPa 520 to 590
1400
Tensile Strength: Yield (Proof), MPa 290 to 330
1050

Thermal Properties

Melting Onset (Solidus), °C 1420 to 1430
1320
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 52
11
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Density, g/cm3 7.9
8.2

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 95
180
Resilience: Unit (Modulus of Resilience), kJ/m3 220 to 290
2510
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 21
47
Strength to Weight: Bending, points 18 to 20
34
Thermal Diffusivity, mm2/s 14
3.0
Thermal Shock Resistance, points 15 to 17
38