ASTM A210 Steel vs. ASTM A203 Steel
Both ASTM A210 steel and ASTM A203 steel are iron alloys.
For each property being compared, the top bar is ASTM A210 steel and the bottom bar is ASTM A203 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 160 | |
| 160 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 34 | |
| 22 to 26 |
| Fatigue Strength, MPa | 230 to 250 | |
| 210 to 280 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 320 to 360 | |
| 330 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 470 to 540 | |
| 520 to 590 |
| Tensile Strength: Yield (Proof), MPa | 290 to 310 | |
| 290 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 to 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 to 53 | |
| 52 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.4 to 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 to 8.1 | |
| 8.5 to 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 3.2 to 4.0 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.6 to 1.7 |
| Embodied Energy, MJ/kg | 18 | |
| 21 to 23 |
| Embodied Water, L/kg | 45 to 46 | |
| 50 to 52 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 160 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 250 | |
| 230 to 410 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 to 19 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 17 to 19 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 15 to 17 | |
| 15 to 17 |