ASTM A210 Steel vs. C97800 Nickel Silver

ASTM A210 steel belongs to the iron alloys classification, while C97800 nickel silver belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A210 steel and the bottom bar is C97800 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
130
Elongation at Break, % 34
10
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
48
Tensile Strength: Ultimate (UTS), MPa 470 to 540
370
Tensile Strength: Yield (Proof), MPa 290 to 310
170

Thermal Properties

Latent Heat of Fusion, J/g 250
220
Maximum Temperature: Mechanical, °C 400
230
Melting Completion (Liquidus), °C 1460 to 1470
1180
Melting Onset (Solidus), °C 1420
1140
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 52 to 53
25
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
4.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0 to 8.1
4.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
40
Density, g/cm3 7.9
8.8
Embodied Carbon, kg CO2/kg material 1.4
5.1
Embodied Energy, MJ/kg 18
76
Embodied Water, L/kg 45 to 46
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140 to 160
31
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 250
120
Stiffness to Weight: Axial, points 13
8.1
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 17 to 19
12
Strength to Weight: Bending, points 17 to 19
13
Thermal Diffusivity, mm2/s 14
7.3
Thermal Shock Resistance, points 15 to 17
13