ASTM A216 Cast Steel vs. SAE-AISI 4150 Steel
Both ASTM A216 cast steel and SAE-AISI 4150 steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A216 cast steel and the bottom bar is SAE-AISI 4150 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 25 to 27 | |
| 12 to 20 |
| Fatigue Strength, MPa | 170 to 230 | |
| 260 to 780 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 570 | |
| 660 to 1310 |
| Tensile Strength: Yield (Proof), MPa | 230 to 310 | |
| 380 to 1220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 420 |
| Melting Completion (Liquidus), °C | 1450 to 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 49 to 52 | |
| 42 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 to 7.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.3 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 2.4 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 18 | |
| 20 |
| Embodied Water, L/kg | 45 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 82 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 250 | |
| 380 to 3930 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 20 | |
| 24 to 47 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 22 to 34 |
| Thermal Diffusivity, mm2/s | 13 to 14 | |
| 11 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 19 to 39 |