ASTM A216 Cast Steel vs. SAE-AISI M3 Class 2 Steel
Both ASTM A216 cast steel and SAE-AISI M3 class 2 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM A216 cast steel and the bottom bar is SAE-AISI M3 class 2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 72 | |
77 |
Tensile Strength: Ultimate (UTS), MPa | 500 to 570 | |
770 to 2210 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
260 |
Melting Completion (Liquidus), °C | 1450 to 1460 | |
1620 |
Melting Onset (Solidus), °C | 1410 | |
1570 |
Specific Heat Capacity, J/kg-K | 470 | |
440 |
Thermal Conductivity, W/m-K | 49 to 52 | |
26 |
Thermal Expansion, µm/m-K | 12 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.8 | |
25 |
Density, g/cm3 | 7.8 | |
8.3 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
12 |
Embodied Energy, MJ/kg | 18 | |
180 |
Embodied Water, L/kg | 45 | |
110 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
23 |
Strength to Weight: Axial, points | 18 to 20 | |
26 to 74 |
Strength to Weight: Bending, points | 18 to 20 | |
22 to 45 |
Thermal Diffusivity, mm2/s | 13 to 14 | |
7.2 |
Thermal Shock Resistance, points | 16 to 18 | |
24 to 69 |