ASTM A217 Cast Steel vs. ASTM A203 Steel
Both ASTM A217 cast steel and ASTM A203 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is ASTM A203 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 210 | |
| 160 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 21 to 27 | |
| 22 to 26 |
| Fatigue Strength, MPa | 200 to 320 | |
| 210 to 280 |
| Poisson's Ratio | 0.28 to 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 to 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
| 520 to 590 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 290 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 410 to 600 | |
| 410 |
| Melting Completion (Liquidus), °C | 1450 to 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 to 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 26 to 50 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 to 9.2 | |
| 7.4 to 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 to 11 | |
| 8.5 to 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 to 7.0 | |
| 3.2 to 4.0 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 2.1 | |
| 1.6 to 1.7 |
| Embodied Energy, MJ/kg | 20 to 28 | |
| 21 to 23 |
| Embodied Water, L/kg | 47 to 87 | |
| 50 to 52 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
| 230 to 410 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 19 to 23 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 6.9 to 14 | |
| 14 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 15 to 17 |