ASTM A217 Cast Steel vs. EN 1.0237 Steel

Both ASTM A217 cast steel and EN 1.0237 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is EN 1.0237 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160 to 210
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21 to 27
20
Fatigue Strength, MPa 200 to 320
250
Poisson's Ratio 0.28 to 0.29
0.29
Shear Modulus, GPa 73 to 75
73
Tensile Strength: Ultimate (UTS), MPa 540 to 710
470
Tensile Strength: Yield (Proof), MPa 270 to 460
360

Thermal Properties

Latent Heat of Fusion, J/g 250 to 270
250
Maximum Temperature: Mechanical, °C 410 to 600
400
Melting Completion (Liquidus), °C 1450 to 1460
1460
Melting Onset (Solidus), °C 1410 to 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26 to 50
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3 to 9.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4 to 11
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4 to 7.0
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5 to 2.1
1.4
Embodied Energy, MJ/kg 20 to 28
18
Embodied Water, L/kg 47 to 87
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 130
88
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 570
340
Stiffness to Weight: Axial, points 13 to 14
13
Stiffness to Weight: Bending, points 24 to 25
24
Strength to Weight: Axial, points 19 to 25
17
Strength to Weight: Bending, points 19 to 23
17
Thermal Diffusivity, mm2/s 6.9 to 14
14
Thermal Shock Resistance, points 16 to 20
15