ASTM A217 Cast Steel vs. Grade 3 Babbitt Metal
ASTM A217 cast steel belongs to the iron alloys classification, while grade 3 Babbitt Metal belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is grade 3 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 to 210 | |
| 27 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 56 |
| Poisson's Ratio | 0.28 to 0.29 | |
| 0.35 |
| Shear Modulus, GPa | 73 to 75 | |
| 21 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 46 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 270 | |
| 79 |
| Melting Completion (Liquidus), °C | 1450 to 1460 | |
| 420 |
| Melting Onset (Solidus), °C | 1410 to 1420 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 230 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 to 7.0 | |
| 70 |
| Density, g/cm3 | 7.8 | |
| 7.4 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 2.1 | |
| 12 |
| Embodied Energy, MJ/kg | 20 to 28 | |
| 200 |
| Embodied Water, L/kg | 47 to 87 | |
| 1210 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
| 19 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 4.2 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 17 |