ASTM A217 Cast Steel vs. SAE-AISI 4130 Steel
Both ASTM A217 cast steel and SAE-AISI 4130 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is SAE-AISI 4130 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 160 to 210 | |
200 to 300 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 21 to 27 | |
13 to 26 |
Fatigue Strength, MPa | 200 to 320 | |
320 to 660 |
Poisson's Ratio | 0.28 to 0.29 | |
0.29 |
Shear Modulus, GPa | 73 to 75 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
530 to 1040 |
Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
440 to 980 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 to 270 | |
250 |
Maximum Temperature: Mechanical, °C | 410 to 600 | |
420 |
Melting Completion (Liquidus), °C | 1450 to 1460 | |
1460 |
Melting Onset (Solidus), °C | 1410 to 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 26 to 50 | |
43 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.3 to 9.2 | |
7.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 to 11 | |
8.3 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.4 to 7.0 | |
2.4 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.5 to 2.1 | |
1.5 |
Embodied Energy, MJ/kg | 20 to 28 | |
20 |
Embodied Water, L/kg | 47 to 87 | |
50 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
83 to 180 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
500 to 2550 |
Stiffness to Weight: Axial, points | 13 to 14 | |
13 |
Stiffness to Weight: Bending, points | 24 to 25 | |
24 |
Strength to Weight: Axial, points | 19 to 25 | |
19 to 37 |
Strength to Weight: Bending, points | 19 to 23 | |
19 to 29 |
Thermal Diffusivity, mm2/s | 6.9 to 14 | |
12 |
Thermal Shock Resistance, points | 16 to 20 | |
16 to 31 |