ASTM A217 Cast Steel vs. SAE-AISI D3 Steel
Both ASTM A217 cast steel and SAE-AISI D3 steel are iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is SAE-AISI D3 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 21 to 27 | |
| 9.8 to 15 |
| Fatigue Strength, MPa | 200 to 320 | |
| 310 to 940 |
| Poisson's Ratio | 0.28 to 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 to 75 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
| 770 to 2050 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 480 to 1550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 270 | |
| 270 |
| Melting Completion (Liquidus), °C | 1450 to 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1410 to 1420 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 26 to 50 | |
| 31 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 to 9.2 | |
| 3.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 to 11 | |
| 3.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 to 7.0 | |
| 8.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 2.1 | |
| 3.2 |
| Embodied Energy, MJ/kg | 20 to 28 | |
| 48 |
| Embodied Water, L/kg | 47 to 87 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 2.5 to 13 | |
| 13 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
| 97 to 180 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 28 to 74 |
| Strength to Weight: Bending, points | 19 to 23 | |
| 24 to 47 |
| Thermal Diffusivity, mm2/s | 6.9 to 14 | |
| 8.3 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 23 to 63 |