ASTM A217 Cast Steel vs. K93600 Alloy
Both ASTM A217 cast steel and K93600 alloy are iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 21 to 27 | |
| 5.0 to 35 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 280 to 750 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 410 to 600 | |
| 440 |
| Melting Onset (Solidus), °C | 1410 to 1420 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 520 |
| Thermal Conductivity, W/m-K | 26 to 50 | |
| 13 |
| Thermal Expansion, µm/m-K | 13 | |
| 7.3 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 to 9.2 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 to 11 | |
| 2.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
| 21 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
| 280 to 2050 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 21 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 19 to 23 | |
| 17 to 24 |
| Thermal Diffusivity, mm2/s | 6.9 to 14 | |
| 3.1 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 34 to 57 |