ASTM A217 Cast Steel vs. R60802 Alloy
ASTM A217 cast steel belongs to the iron alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is ASTM A217 cast steel and the bottom bar is R60802 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 21 to 27 | |
| 22 |
| Poisson's Ratio | 0.28 to 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 to 75 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 710 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 270 to 460 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 to 270 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 26 to 50 | |
| 22 |
| Thermal Expansion, µm/m-K | 13 | |
| 6.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.5 |
| Embodied Water, L/kg | 47 to 87 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 130 | |
| 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 570 | |
| 380 |
| Stiffness to Weight: Axial, points | 13 to 14 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 23 |
| Strength to Weight: Axial, points | 19 to 25 | |
| 18 |
| Strength to Weight: Bending, points | 19 to 23 | |
| 19 |
| Thermal Diffusivity, mm2/s | 6.9 to 14 | |
| 12 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 53 |