ASTM A225 Steel vs. 359.0 Aluminum
ASTM A225 steel belongs to the iron alloys classification, while 359.0 aluminum belongs to the aluminum alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM A225 steel and the bottom bar is 359.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 250 | |
| 90 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 71 |
| Elongation at Break, % | 21 to 23 | |
| 3.8 to 4.9 |
| Fatigue Strength, MPa | 330 to 390 | |
| 100 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 27 |
| Shear Strength, MPa | 390 to 520 | |
| 220 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 830 | |
| 340 to 350 |
| Tensile Strength: Yield (Proof), MPa | 460 to 550 | |
| 250 to 280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 530 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 600 |
| Melting Onset (Solidus), °C | 1420 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 910 |
| Thermal Conductivity, W/m-K | 52 | |
| 140 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 8.0 |
| Embodied Energy, MJ/kg | 24 to 25 | |
| 150 |
| Embodied Water, L/kg | 48 | |
| 1090 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 170 | |
| 12 to 15 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 580 to 820 | |
| 450 to 540 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 54 |
| Strength to Weight: Axial, points | 22 to 29 | |
| 37 to 38 |
| Strength to Weight: Bending, points | 21 to 25 | |
| 42 to 43 |
| Thermal Diffusivity, mm2/s | 14 | |
| 59 |
| Thermal Shock Resistance, points | 18 to 24 | |
| 16 to 17 |