ASTM A225 Steel vs. ASTM B540 Palladium
ASTM A225 steel belongs to the iron alloys classification, while ASTM B540 palladium belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM A225 steel and the bottom bar is ASTM B540 palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 21 to 23 | |
| 1.1 to 14 |
| Fatigue Strength, MPa | 330 to 390 | |
| 350 |
| Poisson's Ratio | 0.29 | |
| 0.38 |
| Shear Modulus, GPa | 73 | |
| 39 |
| Shear Strength, MPa | 390 to 520 | |
| 500 to 700 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 830 | |
| 830 to 1240 |
| Tensile Strength: Yield (Proof), MPa | 460 to 550 | |
| 620 to 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 140 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1220 |
| Melting Onset (Solidus), °C | 1420 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 240 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 4.9 to 5.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 3.5 to 3.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 13 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 170 | |
| 13 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 580 to 820 | |
| 1790 to 4660 |
| Stiffness to Weight: Axial, points | 13 | |
| 4.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 12 |
| Strength to Weight: Axial, points | 22 to 29 | |
| 18 to 27 |
| Strength to Weight: Bending, points | 21 to 25 | |
| 15 to 20 |
| Thermal Shock Resistance, points | 18 to 24 | |
| 41 to 61 |