ASTM A229 Spring Steel vs. 296.0 Aluminum
ASTM A229 spring steel belongs to the iron alloys classification, while 296.0 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM A229 spring steel and the bottom bar is 296.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 490 to 550 | |
| 75 to 90 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 72 |
| Elongation at Break, % | 14 | |
| 3.2 to 7.1 |
| Fatigue Strength, MPa | 710 to 790 | |
| 47 to 70 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 72 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 1690 to 1890 | |
| 260 to 270 |
| Tensile Strength: Yield (Proof), MPa | 1100 to 1230 | |
| 120 to 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 170 |
| Melting Completion (Liquidus), °C | 1450 | |
| 630 |
| Melting Onset (Solidus), °C | 1410 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 870 |
| Thermal Conductivity, W/m-K | 50 | |
| 130 to 150 |
| Thermal Expansion, µm/m-K | 12 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 33 to 37 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 99 to 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 7.8 |
| Embodied Energy, MJ/kg | 19 | |
| 150 |
| Embodied Water, L/kg | 46 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 to 230 | |
| 7.6 to 15 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3260 to 4080 | |
| 110 to 220 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 46 |
| Strength to Weight: Axial, points | 60 to 67 | |
| 24 to 25 |
| Strength to Weight: Bending, points | 40 to 43 | |
| 30 to 31 |
| Thermal Diffusivity, mm2/s | 14 | |
| 51 to 56 |
| Thermal Shock Resistance, points | 54 to 60 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 89 to 94 |
| Carbon (C), % | 0.55 to 0.85 | |
| 0 |
| Copper (Cu), % | 0 | |
| 4.0 to 5.0 |
| Iron (Fe), % | 97.5 to 99 | |
| 0 to 1.2 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.3 to 1.2 | |
| 0 to 0.35 |
| Nickel (Ni), % | 0 | |
| 0 to 0.35 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 2.0 to 3.0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.35 |