ASTM A266 Carbon Steel vs. ASTM Grade LCA Steel

Both ASTM A266 carbon steel and ASTM grade LCA steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A266 carbon steel and the bottom bar is ASTM grade LCA steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21 to 26
27
Fatigue Strength, MPa 170 to 200
170
Poisson's Ratio 0.29
0.29
Reduction in Area, % 34 to 43
40
Shear Modulus, GPa 73
72
Tensile Strength: Ultimate (UTS), MPa 500 to 600
500
Tensile Strength: Yield (Proof), MPa 230 to 290
230

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51 to 52
49
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1 to 8.2
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18 to 19
19
Embodied Water, L/kg 46 to 47
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 230
150
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 21
18
Strength to Weight: Bending, points 18 to 20
18
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 16 to 19
16