ASTM A285 Carbon Steel vs. SAE-AISI 12L14 Steel
Both ASTM A285 carbon steel and SAE-AISI 12L14 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A285 carbon steel and the bottom bar is SAE-AISI 12L14 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 to 130 | |
| 140 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 30 to 34 | |
| 11 to 25 |
| Fatigue Strength, MPa | 150 to 180 | |
| 190 to 290 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 250 to 290 | |
| 280 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 450 | |
| 440 to 620 |
| Tensile Strength: Yield (Proof), MPa | 190 to 230 | |
| 260 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 to 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 53 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 18 |
| Embodied Water, L/kg | 46 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 64 to 93 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 94 to 150 | |
| 180 to 560 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 15 to 22 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 16 to 20 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 12 to 14 | |
| 14 to 20 |