ASTM A299 Steel vs. ZK51A Magnesium
ASTM A299 steel belongs to the iron alloys classification, while ZK51A magnesium belongs to the magnesium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ASTM A299 steel and the bottom bar is ZK51A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 45 |
| Elongation at Break, % | 21 to 22 | |
| 4.7 |
| Fatigue Strength, MPa | 230 to 250 | |
| 62 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 18 |
| Shear Strength, MPa | 370 to 390 | |
| 160 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 620 | |
| 240 |
| Tensile Strength: Yield (Proof), MPa | 330 to 360 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 120 |
| Melting Completion (Liquidus), °C | 1460 | |
| 640 |
| Melting Onset (Solidus), °C | 1420 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 970 |
| Thermal Conductivity, W/m-K | 51 | |
| 110 |
| Thermal Expansion, µm/m-K | 13 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 13 |
| Density, g/cm3 | 7.8 | |
| 1.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 24 |
| Embodied Energy, MJ/kg | 19 | |
| 160 |
| Embodied Water, L/kg | 47 | |
| 940 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 10 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 350 | |
| 260 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 64 |
| Strength to Weight: Axial, points | 21 to 22 | |
| 36 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 47 |
| Thermal Diffusivity, mm2/s | 14 | |
| 61 |
| Thermal Shock Resistance, points | 17 to 18 | |
| 15 |