ASTM A302 Alloy Steel vs. ASTM A387 Grade 9 Steel
Both ASTM A302 alloy steel and ASTM A387 grade 9 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A302 alloy steel and the bottom bar is ASTM A387 grade 9 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 180 to 190 | |
150 to 180 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 20 to 23 | |
20 to 21 |
Fatigue Strength, MPa | 250 to 280 | |
160 to 240 |
Poisson's Ratio | 0.29 | |
0.28 |
Shear Modulus, GPa | 73 | |
75 |
Shear Strength, MPa | 370 to 390 | |
310 to 380 |
Tensile Strength: Ultimate (UTS), MPa | 590 to 620 | |
500 to 600 |
Tensile Strength: Yield (Proof), MPa | 350 to 390 | |
230 to 350 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
270 |
Maximum Temperature: Mechanical, °C | 410 | |
600 |
Melting Completion (Liquidus), °C | 1460 | |
1460 |
Melting Onset (Solidus), °C | 1420 | |
1410 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 39 to 51 | |
26 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.4 | |
9.0 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.4 | |
10 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.4 to 3.0 | |
6.5 |
Density, g/cm3 | 7.8 to 7.9 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.5 to 1.6 | |
2.1 |
Embodied Energy, MJ/kg | 20 to 21 | |
28 |
Embodied Water, L/kg | 48 to 50 | |
87 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
83 to 110 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 410 | |
140 to 310 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 21 to 22 | |
18 to 21 |
Strength to Weight: Bending, points | 20 to 21 | |
18 to 20 |
Thermal Diffusivity, mm2/s | 10 to 14 | |
6.9 |
Thermal Shock Resistance, points | 17 to 18 | |
14 to 17 |