ASTM A302 Alloy Steel vs. C17000 Copper
ASTM A302 alloy steel belongs to the iron alloys classification, while C17000 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM A302 alloy steel and the bottom bar is C17000 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 20 to 23 | |
| 1.1 to 31 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 45 |
| Shear Strength, MPa | 370 to 390 | |
| 320 to 750 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 620 | |
| 490 to 1310 |
| Tensile Strength: Yield (Proof), MPa | 350 to 390 | |
| 160 to 1140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 270 |
| Melting Completion (Liquidus), °C | 1460 | |
| 980 |
| Melting Onset (Solidus), °C | 1420 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 39 to 51 | |
| 110 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.4 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.4 | |
| 22 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 to 7.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.6 | |
| 8.7 |
| Embodied Energy, MJ/kg | 20 to 21 | |
| 140 |
| Embodied Water, L/kg | 48 to 50 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 4.2 to 390 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 410 | |
| 110 to 5420 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 22 | |
| 15 to 41 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 16 to 30 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 32 |
| Thermal Shock Resistance, points | 17 to 18 | |
| 17 to 45 |