ASTM A302 Alloy Steel vs. K94200 Alloy
Both ASTM A302 alloy steel and K94200 alloy are iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is ASTM A302 alloy steel and the bottom bar is K94200 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 20 to 23 | |
| 5.0 to 32 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 54 |
| Shear Strength, MPa | 370 to 390 | |
| 330 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 620 | |
| 500 to 710 |
| Tensile Strength: Yield (Proof), MPa | 350 to 390 | |
| 270 to 650 |
Thermal Properties
| Melting Onset (Solidus), °C | 1420 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 500 |
| Thermal Conductivity, W/m-K | 39 to 51 | |
| 15 |
| Thermal Expansion, µm/m-K | 13 | |
| 5.0 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 to 7.4 | |
| 2.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 to 8.4 | |
| 3.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 to 7.9 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 35 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 410 | |
| 250 to 1460 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.8 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 21 to 22 | |
| 17 to 24 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 17 to 22 |
| Thermal Diffusivity, mm2/s | 10 to 14 | |
| 3.7 |
| Thermal Shock Resistance, points | 17 to 18 | |
| 49 to 70 |