ASTM A356 Grade 9 vs. EN 1.4525 Stainless Steel

Both ASTM A356 grade 9 and EN 1.4525 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A356 grade 9 and the bottom bar is EN 1.4525 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17
5.6 to 13
Fatigue Strength, MPa 310
480 to 540
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 670
1030 to 1250
Tensile Strength: Yield (Proof), MPa 460
840 to 1120

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 440
860
Melting Completion (Liquidus), °C 1470
1430
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 41
18
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 3.6
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.4
2.8
Embodied Energy, MJ/kg 33
39
Embodied Water, L/kg 56
130

Common Calculations

PREN (Pitting Resistance) 4.7
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
68 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 570
1820 to 3230
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
36 to 45
Strength to Weight: Bending, points 22
29 to 33
Thermal Diffusivity, mm2/s 11
4.7
Thermal Shock Resistance, points 19
34 to 41

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.070
Chromium (Cr), % 1.0 to 1.5
15 to 17
Copper (Cu), % 0
2.5 to 4.0
Iron (Fe), % 95.2 to 97.2
70.4 to 79
Manganese (Mn), % 0.5 to 0.9
0 to 1.0
Molybdenum (Mo), % 0.9 to 1.2
0 to 0.8
Nickel (Ni), % 0
3.5 to 5.5
Niobium (Nb), % 0
0 to 0.35
Nitrogen (N), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.2 to 0.6
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0.2 to 0.35
0