ASTM A36 Carbon Steel vs. 5056 Aluminum

ASTM A36 carbon steel belongs to the iron alloys classification, while 5056 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ASTM A36 carbon steel and the bottom bar is 5056 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
67
Elongation at Break, % 22
4.9 to 31
Fatigue Strength, MPa 200
140 to 200
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
25
Shear Strength, MPa 300
170 to 240
Tensile Strength: Ultimate (UTS), MPa 480
290 to 460
Tensile Strength: Yield (Proof), MPa 290
150 to 410

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 400
190
Melting Completion (Liquidus), °C 1460
640
Melting Onset (Solidus), °C 1420
570
Specific Heat Capacity, J/kg-K 470
910
Thermal Conductivity, W/m-K 50
130
Thermal Expansion, µm/m-K 11
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 12
29
Electrical Conductivity: Equal Weight (Specific), % IACS 14
99

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
9.5
Density, g/cm3 7.9
2.7
Embodied Carbon, kg CO2/kg material 1.4
9.0
Embodied Energy, MJ/kg 18
150
Embodied Water, L/kg 44
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 92
12 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 220
170 to 1220
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
51
Strength to Weight: Axial, points 17
30 to 48
Strength to Weight: Bending, points 17
36 to 50
Thermal Diffusivity, mm2/s 14
53
Thermal Shock Resistance, points 16
13 to 20

Alloy Composition

Aluminum (Al), % 0
93 to 95.4
Carbon (C), % 0 to 0.26
0
Chromium (Cr), % 0
0.050 to 0.2
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 99.25 to 100
0 to 0.4
Magnesium (Mg), % 0
4.5 to 5.6
Manganese (Mn), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 0.4
0 to 0.3
Sulfur (S), % 0 to 0.050
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15