ASTM A36 Carbon Steel vs. SAE-AISI 1025 Steel
Both ASTM A36 carbon steel and SAE-AISI 1025 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is ASTM A36 carbon steel and the bottom bar is SAE-AISI 1025 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 | |
| 130 to 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 22 | |
| 17 to 28 |
| Fatigue Strength, MPa | 200 | |
| 190 to 280 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 300 | |
| 290 to 310 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 450 to 500 |
| Tensile Strength: Yield (Proof), MPa | 290 | |
| 250 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 52 |
| Thermal Expansion, µm/m-K | 11 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 18 |
| Embodied Water, L/kg | 44 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 92 | |
| 80 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 170 to 470 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 17 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 16 | |
| 14 to 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.26 | |
| 0.22 to 0.28 |
| Iron (Fe), % | 99.25 to 100 | |
| 99.03 to 99.48 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.050 |