ASTM A369 Grade FP11 vs. EN 1.4406 Stainless Steel

Both ASTM A369 grade FP11 and EN 1.4406 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP11 and the bottom bar is EN 1.4406 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
42
Fatigue Strength, MPa 160
280
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 300
470
Tensile Strength: Ultimate (UTS), MPa 470
680
Tensile Strength: Yield (Proof), MPa 240
320

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 430
950
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
18
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
3.7
Embodied Energy, MJ/kg 21
51
Embodied Water, L/kg 52
150

Common Calculations

PREN (Pitting Resistance) 3.0
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
240
Resilience: Unit (Modulus of Resilience), kJ/m3 150
260
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 17
22
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 14
15

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.030
Chromium (Cr), % 1.0 to 1.5
16.5 to 18.5
Iron (Fe), % 96.1 to 97.7
63.2 to 71.4
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.44 to 0.65
2.0 to 2.5
Nickel (Ni), % 0
10 to 12.5
Nitrogen (N), % 0
0.12 to 0.22
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.5 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015