ASTM A369 Grade FP11 vs. Nickel 242
ASTM A369 grade FP11 belongs to the iron alloys classification, while nickel 242 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is ASTM A369 grade FP11 and the bottom bar is nickel 242.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
220 |
Elongation at Break, % | 20 | |
45 |
Fatigue Strength, MPa | 160 | |
300 |
Poisson's Ratio | 0.29 | |
0.3 |
Shear Modulus, GPa | 73 | |
84 |
Shear Strength, MPa | 300 | |
570 |
Tensile Strength: Ultimate (UTS), MPa | 470 | |
820 |
Tensile Strength: Yield (Proof), MPa | 240 | |
350 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
330 |
Maximum Temperature: Mechanical, °C | 430 | |
930 |
Melting Completion (Liquidus), °C | 1460 | |
1380 |
Melting Onset (Solidus), °C | 1420 | |
1290 |
Specific Heat Capacity, J/kg-K | 470 | |
400 |
Thermal Conductivity, W/m-K | 40 | |
11 |
Thermal Expansion, µm/m-K | 13 | |
11 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
1.4 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
1.4 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.9 | |
75 |
Density, g/cm3 | 7.8 | |
9.0 |
Embodied Carbon, kg CO2/kg material | 1.6 | |
14 |
Embodied Energy, MJ/kg | 21 | |
180 |
Embodied Water, L/kg | 52 | |
290 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 80 | |
300 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 | |
280 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
22 |
Strength to Weight: Axial, points | 17 | |
25 |
Strength to Weight: Bending, points | 17 | |
21 |
Thermal Diffusivity, mm2/s | 11 | |
3.1 |
Thermal Shock Resistance, points | 14 | |
25 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.5 |
Boron (B), % | 0 | |
0 to 0.0060 |
Carbon (C), % | 0.050 to 0.15 | |
0 to 0.030 |
Chromium (Cr), % | 1.0 to 1.5 | |
7.0 to 9.0 |
Cobalt (Co), % | 0 | |
0 to 1.0 |
Copper (Cu), % | 0 | |
0 to 0.5 |
Iron (Fe), % | 96.1 to 97.7 | |
0 to 2.0 |
Manganese (Mn), % | 0.3 to 0.6 | |
0 to 0.8 |
Molybdenum (Mo), % | 0.44 to 0.65 | |
24 to 26 |
Nickel (Ni), % | 0 | |
59.3 to 69 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.030 |
Silicon (Si), % | 0.5 to 1.0 | |
0 to 0.8 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.015 |