ASTM A369 Grade FP11 vs. SAE-AISI 1042 Steel

Both ASTM A369 grade FP11 and SAE-AISI 1042 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A369 grade FP11 and the bottom bar is SAE-AISI 1042 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180 to 200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
14 to 18
Fatigue Strength, MPa 160
230 to 370
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 300
380 to 420
Tensile Strength: Ultimate (UTS), MPa 470
620 to 700
Tensile Strength: Yield (Proof), MPa 240
340 to 580

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 430
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
18
Embodied Water, L/kg 52
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80
87 to 94
Resilience: Unit (Modulus of Resilience), kJ/m3 150
320 to 900
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
22 to 25
Strength to Weight: Bending, points 17
21 to 22
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 14
20 to 22

Alloy Composition

Carbon (C), % 0.050 to 0.15
0.4 to 0.47
Chromium (Cr), % 1.0 to 1.5
0
Iron (Fe), % 96.1 to 97.7
98.5 to 99
Manganese (Mn), % 0.3 to 0.6
0.6 to 0.9
Molybdenum (Mo), % 0.44 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.5 to 1.0
0
Sulfur (S), % 0 to 0.025
0 to 0.050